Fabrication and Characterization of Carbon Black and Phenol Formaldehyde Composites
Received Date: Feb 27, 2018 / Accepted Date: May 28, 2018 / Published Date: Jun 02, 2018
Abstract
Carbon black and Phenol formaldehyde composites were prepared by hot press molding at different temperature (180°C, 200°C, 220°C); pressure (100 kN, 150 kN, 200 kN, 250 kN); heating time (10 min, 20 min, 30 min, 60 min) and several compositions (50%C, 60%C, 70%C, 80%C, 90%C). The different properties such as physical, mechanical, thermal properties were studied by Universal Testing Machine (UTM), Micro hardness tester, TGA/DTA analyser and X-Ray diffractometer etc. In this work, it was observed that the bulk density was slightly changed for 50% carbon black and Phenol formaldehyde composites. Compressive strength of sample was increased with increasing the pressure, heating temperature and time.
Keywords: Carbon black; Phenol formaldehyde; Micro hardness
Citation: Hossain J, Alam MS, Paul SC, Islam S (2018) Fabrication and Characterization of Carbon Black and Phenol Formaldehyde Composites. Ind Chem 4: 127.
Copyright: © 2018 Hossain J, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Share This Article
Recommended Journals
Open Access Journals
Article Usage
- Total views: 5725
- [From(publication date): 0-2018 - Nov 21, 2024]
- Breakdown by view type
- HTML page views: 4977
- PDF downloads: 748