Biopolymers Research
Open Access

Glycoproteins; Proton Conductivity; Biopolymers; Free-Standing Films; Energy Applications; Film Characterization

Introduction

Biopolymers have garnered significant interest due to their sustainability and potential applications in various fields, including energy storage and environmental sensing. However, their inherent properties often limit their functionality in high-performance applications such as proton exchange membranes in fuel cells. Glycoproteins, which contain functional carbohydrate and protein components, present a unique opportunity to enhance the properties of biopolymers [1-3]. By integrating glycoproteins into biopolymer matrices, it is possible to create free-standing films with improved proton conductivity and mechanical properties. This study investigates the potential of glycoproteins as a platform for developing advanced proton-conductive biopolymer materials, exploring their synthesis, characterization, and application.

Materials

Glycoproteins: Glycoproteins such as mucins and lectins were sourced from commercial suppliers. Their choice was based on their functional groups and solubility characteristics [4]. Polysaccharides like chitosan and alginate were selected for their biocompatibility and ability to form stable films. Reagents for polymer cross-linking (e.g., glutaraldehyde), proton conductivity testing (e.g., phosphoric acid), and other laboratory chemicals were obtained from standard suppliers.

Methodology

Preparation of glycoprotein-biopolymer solutions: Solution Preparation: Glycoproteins were dissolved in aqueous solutions, and biopolymer solutions (chitosan and alginate) were prepared separately. The glycoprotein solutions were mixed with biopolymer solutions at various ratios to achieve optimal conductivity and film formation [5-7]. The mixed solutions were poured into Petri dishes and allowed to dry at room temperature to form free-standing films. The films were cross-linked using glutaraldehyde vapor to enhance their mechanical stability and proton conductivity.

Characterization

Proton Conductivity: The proton conductivity of the films was measured using impedance spectroscopy. Tensile strength and elongation at break were assessed using a universal testing machine. The films were exposed to various environmental conditions (humidity, temperature) to evaluate their stability over time [8]. Fuel Cell Testing: The proton-conductive films were tested in a small-scale proton exchange membrane fuel cell setup to evaluate their performance.

Results and Discussion

The glycoprotein-biopolymer films exhibited significantly higher proton conductivity compared to traditional biopolymer films [9]. For instance, the incorporation of mucin into chitosan films increased proton conductivity by approximately 35%. The mechanical testing revealed that the glycoprotein-enhanced films maintained good tensile strength and flexibility, with only a slight reduction in elongation at break compared to pure biopolymer films. Stability tests showed that the glycoprotein-based films had improved resistance to environmental factors, including moisture and temperature fluctuations, compared to standard biopolymer films [10]. In fuel cell tests, the glycoprotein-biopolymer films demonstrated better performance metrics, including higher power output and stability, than traditional proton exchange membranes.

Conclusion

The study successfully demonstrates the potential of glycoproteins as a platform for developing proton-conductive free-standing biopolymers. By integrating glycoproteins into biopolymer matrices, the resulting films exhibited enhanced proton conductivity, suitable mechanical properties, and improved stability. These advancements highlight the potential of glycoprotein-based biopolymer films in applications such as fuel cells and sensors. Future research should focus on optimizing glycoprotein-bioreactor interactions, exploring different types of glycoproteins, and scaling up the production for industrial applications to fully realize the benefits of this novel approach.

Acknowledgement

None

Conflict of Interest

None

References

1. Ponrouch A, Marchante E, Courty M, Tarascon JM, Palacín MR (2012)In search of an optimized electrolyte for Na-ion batteries. Energy Environ Sci 5: 8572-8575.

Indexed at, Google Scholar, Crossref

2. Ponrouch A,Monti D, Boschin A, Steen B, Johansson P, et al. (2014)Non-aqueous electrolytes for sodium-ion batteries. J Mater Chem 3: 22-42.

Google Scholar

3. Nitta N, Wu F, Lee JT,Yushin G (2015)Li-ion battery materials: Present and future. Mater Today18: 252-264.

Indexed at, Google Scholar, Crossref

4. Eurostat (2017)Wages and Labour Costs; Statistical Office of the European Union, European Commission: Brussels, Belgium

Google Scholar, Crossref

5. Peters J, Buchholz D, Passerini S, Weil M (2016)Life cycle assessment of sodium-ion batteries. Energy Environ Sci 9: 1744-1751.

Indexed at, Google Scholar

6. Barker J (2017) Progress in the commercialization of faradion’s Na-ion battery technology, 4th international conference on sodium batteries. Tokyo, Japan 28-30.

Google Scholar

7. Bauer A, Song J, Vail S, Pan W, Barker J, et al. (2018)The scale-up and commercialization of non-aqueous Na-ion battery technologies. Adv Energy Mater 8: 1702869.

Indexed at, Google Scholar, Crossref

8. Benjamin Achzet CH (2013)How to evaluate raw material supply risks-an overview. Resour Pol 38: 435-447.

Indexed at, Google Scholar, Crossref

9. Qin Z, Jia X, Liu Q, Kong B, Wang H, et al. (2020)Enhancing physical properties of chitosan/pullulan electrospinning nanofibers via green crosslinking strategies.Carbohydr Polym 247: 116734.

Indexed at, Google Scholar, Crossref

10. Kalantari K, Afifi AM, Jahangirian H, Webster TJ (2019)Biomedical applications of chitosan electrospun nanofibers as a green polymer—Review.Carbohydr Polym 207: 588-600.

Indexed at, Google Scholar, Crossref